長期供應MDPE L 3810X03原材料 ！關于L 3810X03注塑溫度(成型溫度),L 3810X03縮水率,L 3810X03流動性等相關參數請參照量子化學廠家提供的物性表數據。
1、ABS/AS-0130M/三星第一毛織
2、ABS/683 FR/美國RTP
3、PVC/30BKA488/普立萬
4、HDPE/XS 10 BRS/法國道達爾 污水處理
5、LLDPE/2020SB/日本普瑞曼 沖擊強度、成型性、透明性 沙拉醬容器、吹制管子、洗滌劑容器、化裝品容器
6、PET/835R/泰科納
7、PVC/12802/喬治亞海灣
8、LLDPE/1018G/日本普瑞曼 低抗氧劑含量、耐低溫沖擊
9、PBT/J600/泰科納 40%增強
10、PP/5E17V/美國陶氏
以下數據由:PBT塑料膠粒 //shanglikaiguan.cn/ 提供
| 其它 其它 擠出 | |
| 袋 | |
| 共聚物，與食物接觸的可接受的 | |
| 性能項目 | 試驗條件[狀態] | 測試方法 | 測試數據 | ||
| 密度 | ASTM D-1505 | 0.940 | g/cm3 | ||
| 熔體流動速率 | ASTM D-1238 | 0.10 | g/10min | ||
| 切割模量(TD) | ASTM D-882 | 855 | MPa | ||
| 切割模量(MD) | ASTM D-882 | 662 | MPa | ||
| 屈服拉伸強度(TD) | ASTM D-882 | 27.6 | MPa | ||
| 屈服拉伸強度(MD) | ASTM D-882 | 23.4 | MPa | ||
| 斷裂拉伸強度(TD) | ASTM D-882 | 46.2 | MPa | ||
| 斷裂拉伸強度(MD) | ASTM D-882 | 66.2 | MPa | ||
| 斷裂伸長率(TD) | ASTM D-882 | 620 | % | ||
| 斷裂伸長率(MD) | ASTM D-882 | 380 | % | ||
| 落鏢沖擊強度 | ASTM D-1709 | 76 | g | ||
| 埃爾曼多夫撕裂強度(TD) | ASTM D-1922 | 560 | g | ||
| 埃爾曼多夫撕裂強度(MD) | ASTM D-1922 | 16 | g | ||
| 密度 | ASTM D-1505 | 0.924 | g/cm3 | ||
| 熔體流動速率 | 190℃/2.16kg | ASTM D-1238 | 3 | g/10min | |
| 薄膜厚度-Tested | 31.8 | um | |||
| 割線模量-1% Secant(TD) | 31.8um，Blown Film | ASTM D-882 | 172 | MPa | |
| 割線模量-1% Secant(MD) | 31.8um，Blown Film | ASTM D-882 | 159 | MPa | |
| 割線模量-1% Secant(TD) | 31.8um，Blown Film | ASTM D-882 | 197 | MPa | |
| 割線模量-1% Secant(MD) | 31.8um，Blown Film | ASTM D-882 | 208 | MPa | |
| 拉伸屈服強度(TD) | 31.8um，Blown Film | ASTM D-882 | 10.7 | MPa | |
| 拉伸屈服強度(MD) | 31.8um，Blown Film | ASTM D-882 | 10.9 | MPa | |
| 拉伸屈服強度(TD) | 31.8um，Blown Film | ASTM D-882 | 9.31 | MPa | |
| 拉伸屈服強度(MD) | 31.8um，Blown Film | ASTM D-882 | 9.38 | MPa | |
| 拉抻斷裂強度(TD) | 31.8um，Blown Film | ASTM D-882 | 17.2 | MPa | |
| 拉抻斷裂強度(MD) | 31.8um，Blown Film | ASTM D-882 | 18.6 | MPa | |
| 拉抻斷裂強度(TD) | 31.8um，Blown Film | ASTM D-882 | 17 | MPa | |
| 拉抻斷裂強度(MD) | 31.8um，Blown Film | ASTM D-882 | 29.1 | MPa | |
| 拉伸斷裂伸長率(MD) | 31.8um，Blown Film | ASTM D-882 | 200 | % | |
| 拉伸斷裂伸長率(TD) | 31.8um，Blown Film | ASTM D-882 | 500 | % | |
| 拉伸斷裂伸長率(MD) | 31.8um，Blown Film | ASTM D-882 | 230 | % | |
| 拉伸斷裂伸長率(TD) | 31.8um，Blown Film | ASTM D-882 | 610 | % | |
| 落錘沖擊 | 31.8um，Blown Film | ASTM D-1709 | 65 | g | |
| 落錘沖擊 | 31.8um，Blown Film | ASTM D-1709 | 110 | g | |
| 埃爾曼多夫撕裂強度(MD) | 31.8um，Blown Film | ASTM D-1922 | 270 | g | |
| 埃爾曼多夫撕裂強度(TD) | 31.8um，Blown Film | ASTM D-1922 | 170 | g | |
| 埃爾曼多夫撕裂強度(MD) | 31.8um，Blown Film | ASTM D-1922 | 300 | g | |
| 埃爾曼多夫撕裂強度(TD) | 31.8um，Blown Film | ASTM D-1922 | 160 | g | |
| 光澤度 | 45°，31.8um，Blown Film | ASTM D-2457 | 70 | ||
| 光澤度 | 31.8um，Cast Film | ASTM D-2457 | 77 | ||
| 霧度 | 31.7um，Blown Film | ASTM D-1003 | 5.4 | % | |
| 霧度 | 31.7um，Cast Film | ASTM D-1003 | 3.4 | % | |
| 關于量子化學 L 3810X03價格 | |||||
| 1.有關“MDPE 量子化學 L 3810X03”物性表及MDPE塑料原料價格以出廠實時數據為準. 2.更多塑料原料行情敬請關注我們的資訊動態. | |||||